TY - CHAP A1 - Kasch, Susanne A1 - Schmidt, Thomas A1 - Eichler, Fabian A1 - Thurn, Laura A1 - Jahn, Simon A1 - Bremen, Sebastian T1 - Solution approaches and process concepts for powder bed-based melting of glass T2 - Industrializing Additive Manufacturing. Proceedings of AMPA2020 N2 - In the study, the process chain of additive manufacturing by means of powder bed fusion will be presented based on the material glass. In order to reliably process components additively, new concepts with different solutions were developed and investigated. Compared to established metallic materials, the properties of glass materials differ significantly. Therefore, the process control was adapted to the material glass in the investigations. With extensive parameter studies based on various glass powders such as borosilicate glass and quartz glass, scientifically proven results on powder bed fusion of glass are presented. Based on the determination of the particle properties with different methods, extensive investigations are made regarding the melting behavior of glass by means of laser beams. Furthermore, the experimental setup was steadily expanded. In addition to the integration of coaxial temperature measurement and regulation, preheating of the building platform is of major importance. This offers the possibility to perform 3D printing at the transformation temperatures of the glass materials. To improve the component’s properties, the influence of a subsequent heat treatment was also investigated. The experience gained was incorporated into a new experimental system, which allows a much better exploration of the 3D printing of glass. Currently, studies are being conducted to improve surface texture, building accuracy, and geometrical capabilities using three-dimensional specimen. The contribution shows the development of research in the field of 3D printing of glass, gives an insight into the machine and process engineering as well as an outlook on the possibilities and applications. KW - Glass powder KW - Laser processing KW - Additive manufacturing KW - Melting KW - L-PBF Y1 - 2020 SN - 978-3-030-54333-4 (Print) SN - 978-3-030-54334-1 (Online) U6 - http://dx.doi.org/10.1007/978-3-030-54334-1_7 N1 - International Conference on Additive Manufacturing in Products and Applications. 01.-03. September 2020. Zurich, Switzerland SP - 82 EP - 95 PB - Springer CY - Cham ER - TY - JOUR A1 - Raffeis, Iris A1 - Adjei-Kyeremeh, Frank A1 - Vroomen, Uwe A1 - Westhoff, Elmar A1 - Bremen, Sebastian A1 - Hohoi, Alexandru A1 - Bührig-Polaczek, Andreas T1 - Qualification of a Ni-Cu alloy for the laser powder bed fusion process (LPBF): Its microstructure and mechanical properties JF - Applied Sciences N2 - As researchers continue to seek the expansion of the material base for additive manufacturing, there is a need to focus attention on the Ni–Cu group of alloys which conventionally has wide industrial applications. In this work, the G-NiCu30Nb casting alloy, a variant of the Monel family of alloys with Nb and high Si content is, for the first time, processed via the laser powder bed fusion process (LPBF). Being novel to the LPBF processes, optimum LPBF parameters were determined, and hardness and tensile tests were performed in as-built conditions and after heat treatment at 1000 °C. Microstructures of the as-cast and the as-built condition were compared. Highly dense samples (99.8% density) were achieved after varying hatch distance (80 µm and 140 µm) with scanning speed (550 mm/s–1500 mm/s). There was no significant difference in microhardness between varied hatch distance print sets. Microhardness of the as-built condition (247 HV0.2) exceeded the as-cast microhardness (179 HV0.2.). Tensile specimens built in vertical (V) and horizontal (H) orientations revealed degrees of anisotropy and were superior to conventionally reported figures. Post heat treatment increased ductility from 20% to 31% (V), as well as from 16% to 25% (H), while ultimate tensile strength (UTS) and yield strength (YS) were considerably reduced. Y1 - 2020 U6 - http://dx.doi.org/10.3390/app10103401 SN - 2076-3417 N1 - Special Issue Materials Development by Additive Manufacturing Techniques VL - 10 IS - Art. 3401 SP - 1 EP - 15 PB - MDPI CY - Basel ER -