TY  - CHAP
A1  - Eichler, Fabian
A1  - Skupin, Marco
A1  - Thurn, Laura
A1  - Kasch, Susanne
A1  - Schmidt, Thomas
T1  - Operating limits for beam melting of glass materials
T2  - Modern Technologies in Manufacturing (MTeM 2019)
N2  - Laser-based Additive Manufacturing (AM) processes for the use of metals out of the powder bed have been investigated profusely and are prevalent in industry. Although there is a broad field of application, Laser Powder Bed Fusion (LPBF), also known as Selective Laser Melting (SLM) of glass is not fully developed yet. The material properties of glass are significantly different from the investigated metallic material for LPBF so far. As such, the process cannot be transferred, and the parameter limits and the process sequence must be redefined for glass. Starting with the characterization of glass powders, a parameter field is initially confined to investigate the process parameter of different glass powder using LPBFprocess. A feasibility study is carried out to process borosilicate glass powder. The effects of process parameters on the dimensional accuracy of fabricated parts out of borosilicate and hints for the post-processing are analysed and presented in this paper.
Y1  - 2019
U6  - http://dx.doi.org/10.1051/matecconf/201929901004
N1  - MATEC Web of Conferences 299; MTeM 2019
VL  - 299
IS  - Article 01004
ER  - 
TY  - JOUR
A1  - Abbas, Karim
A1  - Balc, Nicolae
A1  - Bremen, Sebastian
A1  - Skupin, Marco
T1  - Crystallization and aging behavior of polyetheretherketone PEEK within rapid tooling and rubber molding
JF  - Journal of Manufacturing and Materials Processing
N2  - In times of short product life cycles, additive manufacturing and rapid tooling are important methods to make tool development and manufacturing more efficient. High-performance polymers are the key to mold production for prototypes and small series. However, the high temperatures during vulcanization injection molding cause thermal aging and can impair service life. The extent to which the thermal stress over the entire process chain stresses the material and whether it leads to irreversible material aging is evaluated. To this end, a mold made of PEEK is fabricated using fused filament fabrication and examined for its potential application. The mold is heated to 200 ◦C, filled with rubber, and cured. A differential scanning calorimetry analysis of each process step illustrates the crystallization behavior and first indicates the material resistance. It shows distinct cold crystallization regions at a build chamber temperature of 90 ◦C. At an ambient temperature above Tg, crystallization of 30% is achieved, and cold crystallization no longer occurs. Additional tensile tests show a decrease in tensile strength after ten days of thermal aging. The steady decrease in recrystallization temperature indicates degradation of the additives. However, the tensile tests reveal steady embrittlement of the material due to increasing crosslinking.
KW  - additive manufacturing
KW  - fused filament fabrication
KW  - crystallization
KW  - polyetheretherketone
KW  - rapid tooling
Y1  - 2022
U6  - http://dx.doi.org/10.3390/jmmp6050093
SN  - 2504-4494
N1  - The article belongs to the Special Issue Advances in Injection Molding: Process, Materials and Applications
VL  - 6
IS  - 5
SP  - 1
EP  - 12
PB  - MDPI
CY  - Basel
ER  -