TY - BOOK ED - Raatschen, Hans-Jürgen T1 - Ingenieurfreunde FH Aachen : 75 Jahre Förderverein; Elektrotechnik und Informationstechnik, Luft- und Raumfahrttechnik, Maschinenbau und Mechatronik / [Hrsg.: Ingenieurfreunde FH Aachen e. V. ; Red.: H. J. Raatschen] Y1 - 2010 SN - 978-3-941704-03-9 PB - Klinkenberg CY - Aachen ER - TY - JOUR A1 - Gebhardt, Andreas A1 - Schmidt, Frank-Michael A1 - Hötter, Jan-Steffen A1 - Sokalla, Wolfgang A1 - Sokalla, Patrick T1 - Additive Manufacturing by selective laser melting the realizer desktop machine and its application for the dental industry JF - Physics Procedia Y1 - 2010 SN - 1875-3892 N1 - Laser Assisted Net Shape Engineering 6, Proceedings of the LANE 2010, Part 2 VL - 5 IS - 2 SP - 543 EP - 549 ER - TY - JOUR A1 - Haselgruber, Nikolaus A1 - Mautner, Karin A1 - Thiele, Jan T1 - Usage Space Analysis for Reliability Testing JF - Quality and Reliability Engineering International N2 - During the development process of a complex technical product, one widely used and important technique is accelerated testing where the applied stress on a component is chosen to exceed the reference stress, i.e. the stress encountered in field operation, in order to reduce the time to failure. For that, the reference stress has to be known. Since a complex technical product may fail regarding numerous failure modes, stress in general is highly dimensional rather than scalar. In addition, customers use their products individually, i.e. field operation should be described by a distribution rather than by one scalar stress value. In this paper, a way to span the customer usage space is shown. It allows the identification of worst case reference stress profiles in significantly reduced dimensions with minimal loss of information. The application example shows that even for a complex product like a combustion engine, stress information can be compressed significantly. With low measurement effort it turned out that only three reference stress cycles were sufficient to cover a broad range of customer stress variety. Y1 - 2010 U6 - https://doi.org/10.1002/qre.1155 SN - 1099-1638 N1 - Special Issue: Business and Industrial Statistics: Developments and Industrial Practices in Quality and Reliability VL - 26 IS - 8 SP - 877 EP - 885 PB - Wiley CY - New York ER - TY - CHAP A1 - Raatschen, Hans-Jürgen T1 - Von der Königlichen Höheren Maschinenbauschule Aachen zu den Ingenieurfachbereichen der FH Aachen T2 - Ingenieurfreunde FH Aachen : 75 Jahre Förderverein; Elektrotechnik und Informationstechnik, Luft- und Raumfahrttechnik, Maschinenbau und Mechatronik KW - Geschichte Y1 - 2010 SN - 978-3-941704-03-9 SP - 13 EP - 18 PB - Klinkenberg CY - Aachen ER - TY - CHAP A1 - Raatschen, Hans-Jürgen T1 - 75 Jahre Vereinsgeschichte T2 - Ingenieurfreunde FH Aachen : 75 Jahre Förderverein; Elektrotechnik und Informationstechnik, Luft- und Raumfahrttechnik, Maschinenbau und Mechatronik KW - Geschichte Y1 - 2010 SN - 978-3-941704-03-9 SP - 66 EP - 72 PB - Klinkenberg CY - Aachen ER - TY - CHAP A1 - Reisgen, Uwe A1 - Schleser, Markus A1 - Harms, Alexander A1 - Schiebahn, Alexander T1 - Konduktiv unterstütztes Rührreibschweißen an Stahl- und Aluminiumwerkstoffen T2 - DVS congress 2010 : Große Schweißtechnische Tagung ; Studentenkongress ; Statusseminar "Schneidtechnik" ; Abschlusskolloquium zum AiF-Forschungscluster "Integration des Rührreibschweißens in Fertigungsprozessketten" ; Vorträge der Veranstaltung in Nürnberg am 27. und 28. September 2010. (DVS-Berichte ; 267) Y1 - 2010 SN - 978-3-87155-592-3 SP - 394 EP - 398 PB - DVS Media CY - Düsseldorf ER - TY - JOUR A1 - Reisgen, Uwe A1 - Schleser, Markus A1 - Mokrov, Oleg A1 - Ahmed, Essam T1 - Uni- and bi-axial deformation behavior of laser welded advanced high strength steel sheets JF - Journal of materials processing technology N2 - Bead-on-plate butt joints of 2.5 mm hot rolled DP600/DP600 and 1.2 mm cold rolled TRIP700/TRIP700 steel sheets were performed using 6 kW CO2 laser beam welding. The welding speed ranged from 1.5 to 3.0 and from 2.1 to 3.9 m/min in DP/DP and TRIP/TRIP steel weldments respectively. A top surface helium gas was used as a shielding gas at a flow rate of 20 l/min. Metallographic examinations and transverse tensile testing (DIN EN 895: 1995) were carried out to characterize the weldments. The formability of base metals and weldments were investigated by standard Erichsen test (DIN EN ISO 20482). It was found that the uniaxial plastic behavior of both DP600 and TRIP700 base metals was in agreement with Swift and modified Mecking–Kocks models respectively. In a perpendicular tensile test to the weld line, all specimens were fractured at the base metal however the strengths were somewhat higher than those of base metal. There was a significant reduction in formability caused by welding of both DP/DP and TRIP/TRIP steel weldments and the formability has been improved with the increase of the welding speed. Y1 - 2010 U6 - https://doi.org/http10.1016/j.jmatprotec.2010.08.003 SN - 0924-0136 VL - 210 IS - 15 SP - 2188 EP - 2196 PB - Elsevier CY - Amsterdam ER - TY - CHAP A1 - Reisgen, Uwe A1 - Schleser, Markus A1 - Stieglitz, Anja T1 - Kleben in anspruchsvollen Anwendungsbereichen T2 - Jahrbuch Schweißtechnik 2011 Y1 - 2010 SN - 0935-0292 SP - 226 EP - 235 PB - DVS CY - Düsseldorf ER - TY - CHAP A1 - Reisgen, Uwe A1 - Schoene, Jens A1 - Schleser, Markus A1 - Jerabek, Jakub A1 - Keil, Allessandra ED - Brameshuber, Wolfgang T1 - Theoretical and experimental investigations on textile-reinforced concrete spalling behavior T2 - Textile reinforced concrete : 2nd ICTRC : International RILEM Conference on Material Science : Aachen Germany, September 6 - 8, 2010. Vol. 1. (RILEM Proceedings PRO ; 75) Y1 - 2010 SN - 978-2-35158-106-3 SP - 153 EP - 162 PB - RILEM Publ. CY - Bagneux ER - TY - JOUR A1 - Mukherjee, Krishnendu A1 - Prahl, Ulrich A1 - Bleck, Wolfgang A1 - Reisgen, Uwe A1 - Schleser, Markus A1 - Abdurakhmanov, Aydemir T1 - Characterization and modelling techniques for gas metal arc welding of DP 600 sheet steels JF - Materialwissenschaft und Werkstofftechnik N2 - The objectives of the present work are to characterize the Gas Metal Arc Welding process of DP 600 sheet steel and to summarize the modelling techniques. The time-temperature evolution during the welding cycle was measured experimentally and modelled with the softwaretool SimWeld. To model the phase transformations during the welding cycle dilatometer tests were done to quantify the parameters for phase field modelling by MICRESS®. The important input parameters are interface mobility, nucleation density, etc. A contribution was made to include austenite to bainite transformation in MICRESS®. This is useful to predict the microstructure in the fast cooling segments. The phase transformation model is capable to predict the microstructure along the heating and cooling cycles of welding. Tensile tests have shown the evidence of failure at the heat affected zone, which has the ferrite-tempered martensite microstructure. Y1 - 2010 U6 - https://doi.org/10.1002/mawe.201000692 SN - 1521-4052 VL - 41 IS - 11 SP - 972 EP - 983 PB - Wiley-VCH CY - Weinheim ER -