Selective Laser Melting (SLM) is one of the Additive Manufacturing (AM) technologies applicable for producing complex geometries which are typically expensive or difficult to fabricate using conventional methods. This process has been extensively investigated experimentally for various metals and the fabrication process parameters have been established for different applications; however, fabricating 3D glass objects using SLM technology has remained a challenge so far although it could have many applications. This paper presents a summery on various experimental evaluations of a material database incorporating the build parameters of glass powder using the SLM process for jewelry applications.
The aim of this work was to perform a detailed investigation of the use of Selective Laser Melting (SLM) technology to process eutectic silver-copper alloy Ag 28 wt. % Cu (also called AgCu28). The processing occurred with a Realizer SLM 50 desktop machine. The powder analysis (SEM-topography, EDX, particle distribution) was reported as well as the absorption rates for the near-infrared (NIR) spectrum. Microscope imaging showed the surface topography of the manufactured parts. Furthermore, microsections were conducted for the analysis of porosity. The Design of Experiments approach used the response surface method in order to model the statistical relationship between laser power, spot distance and pulse time.
The rail business is challenged by long product life cycles and a broad spectrum of assembly groups and single parts. When spare part obsolescence occurs, quick solutions are needed. A reproduction of obsolete parts is often connected to long waiting times and minimum lot quantities that need to be purchased and stored. Spare part storage is therefore challenged by growing stocks, bound capital and issues of part ageing. A possible solution could be a virtual storage of spare parts which will be 3D printed through additive manufacturing technologies in case of sudden demand. As mechanical properties of additive manufactured parts are neither guaranteed by machine manufacturers nor by service providers, the utilization of this relatively young technology is impeded and research is required to address these issues. This paper presents an examination of mechanical properties of specimens manufactured from stainless steel through the selective laser melting (SLM) process. The specimens were produced in multiple batches. This paper interrogates the question if the test results follow a normal distribution pattern and if mechanical property predictions can be made. The results will be put opposite existing threshold values provided as the industrial standard. Furthermore, probability predictions will be made in order to examine the potential of the SLM process to maintain state-of-the-art mechanical property requirements.
Additive manufacturing (AM) works by creating objects layer by layer in a manner similar to a 2D printer with the “printed” layers stacked on top of each other. The layer-wise manufacturing nature of AM enables fabrication of freeform geometries which cannot be fabricated using conventional manufacturing methods as a one part. Depending on how each layer is created and bonded to the adjacent layers, different AM methods have been developed. In this chapter, the basic terms, common materials, and different methods of AM are described, and their potential applications are discussed.
Rapid Tooling
(2019)
Improving the Mechanical Strength of Dental Applications and Lattice Structures SLM Processed
(2020)
To manufacture custom medical parts or scaffolds with reduced defects and high mechanical characteristics, new research on optimizing the selective laser melting (SLM) parameters are needed. In this work, a biocompatible powder, 316L stainless steel, is characterized to understand the particle size, distribution, shape and flowability. Examination revealed that the 316L particles are smooth, nearly spherical, their mean diameter is 39.09 μm and just 10% of them hold a diameter less than 21.18 μm. SLM parameters under consideration include laser power up to 200 W, 250–1500 mm/s scanning speed, 80 μm hatch spacing, 35 μm layer thickness and a preheated platform. The effect of these on processability is evaluated. More than 100 samples are SLM-manufactured with different process parameters. The tensile results show that is possible to raise the ultimate tensile strength up to 840 MPa, adapting the SLM parameters for a stable processability, avoiding the technological defects caused by residual stress. Correlating with other recent studies on SLM technology, the tensile strength is 20% improved. To validate the SLM parameters and conditions established, complex bioengineering applications such as dental bridges and macro-porous grafts are SLM-processed, demonstrating the potential to manufacture medical products with increased mechanical resistance made of 316L.