Bead-on-plate butt joints of 2.5 mm hot rolled DP600/DP600 and 1.2 mm cold rolled TRIP700/TRIP700 steel sheets were performed using 6 kW CO2 laser beam welding. The welding speed ranged from 1.5 to 3.0 and from 2.1 to 3.9 m/min in DP/DP and TRIP/TRIP steel weldments respectively. A top surface helium gas was used as a shielding gas at a flow rate of 20 l/min. Metallographic examinations and transverse tensile testing (DIN EN 895: 1995) were carried out to characterize the weldments. The formability of base metals and weldments were investigated by standard Erichsen test (DIN EN ISO 20482). It was found that the uniaxial plastic behavior of both DP600 and TRIP700 base metals was in agreement with Swift and modified Mecking–Kocks models respectively. In a perpendicular tensile test to the weld line, all specimens were fractured at the base metal however the strengths were somewhat higher than those of base metal. There was a significant reduction in formability caused by welding of both DP/DP and TRIP/TRIP steel weldments and the formability has been improved with the increase of the welding speed.
The objectives of the present work are to characterize the Gas Metal Arc Welding process of DP 600 sheet steel and to summarize the modelling techniques. The time-temperature evolution during the welding cycle was measured experimentally and modelled with the softwaretool SimWeld. To model the phase transformations during the welding cycle dilatometer tests were done to quantify the parameters for phase field modelling by MICRESS®. The important input parameters are interface mobility, nucleation density, etc. A contribution was made to include austenite to bainite transformation in MICRESS®. This is useful to predict the microstructure in the fast cooling segments. The phase transformation model is capable to predict the microstructure along the heating and cooling cycles of welding. Tensile tests have shown the evidence of failure at the heat affected zone, which has the ferrite-tempered martensite microstructure.
This paper aims to evaluate the formability of tailor welded blanks of dual phase (DP600)/transformation induced plasticity (TRIP700) steel sheets. In this work, bead on plate butt joints of 2·5 mm DP600 and 1·2 mm TRIP700 steel sheets were performed using CO2 laser beam welding. Microhardness measurements and transverse tensile testing were carried out to characterise the welds. The formability of base metals and welds were investigated by standard Erichsen test. In a perpendicular tensile test to the weld line, all specimens were fractured at the TRIP base metal, and the strengths were somewhat higher than those of base metal. There was a significant reduction in formability caused by welding of the DP600/TRIP700 steel sheets, and the formability increased with increasing welding speed.
Shielding gas influences on laser weldability of tailored blanks of advanced automotive steels
(2010)
The effects of shielding gas types and flow rates on CO2 laser weldability of DP600/TRIP700 steel sheets were studied in this work. The evaluated shielding gases were helium (He), argon (Ar) and different mixtures of He and Ar. Weld penetration, tensile strength and formability (Erichsen test) of laser welds were found to be strongly dependent upon the shielding gas types. The ability of shielding gas in removing plasma plume and thus increasing weld penetration is believed to be closely related to ionization potential and atomic weight which determine the period of plasma formation and disappearance. It was found that the higher helium shielding gas flow rate, the deeper weld penetration and the lower weld width.
Numerical and experimental investigation of tensile behavior of laser beam welded TRIP700 steel
(2011)
Application of polymers in textile reinforced concrete : from the interface to construction elements
(2006)
Composite improvement of textile reinforced concrete by polymeric impregnation of the textiles
(2006)
In this research work, a statistical analysis of the CO2 laser beam welding of dual phase (DP600)/transformation induced plasticity (TRIP700) steel sheets was done using response surface methodology. The analysis considered the effect of laser power (2–2.2 kW), welding speed (40–50 mm/s) and focus position (−1 to 0 mm) on the heat input, the weld bead geometry, uniaxial tensile strength, formability limited dome height and welding operation cost. The experimental design was based on Box–Behnken design using linear and quadratic polynomial equations for predicting the mathematical models. The results indicate that the proposed models predict the responses adequately within the limits of welding parameters being used and the welding speed is the most significant parameter during the welding process.
Generally, the quality of a weld joint is directly influenced by the welding input parameter settings. Selection of proper process parameters is important to obtain the desired weld bead profile and quality. In this research work, numerical and graphical optimization techniques of the CO2 laser beam welding of dual phase (DP600)/transformation induced plasticity (TRIP700) steel sheets were carried out using response surface methodology (RSM) based on Box–Behnken design. The procedure was established to improve the weld quality, increase the productivity and minimize the total operation cost by considering the welding parameters range of laser power (2–2.2 kW), welding speed (40–50 mm/s) and focus position (−1 to 0 mm). It was found that, RSM can be considered as a powerful tool in experimental welding optimization, even when the experimenter does not have a model for the process. Strong, efficient and low cost weld joints could be achieved using the optimum welding conditions.
Electron beam plasma measurement was realised by means of DIABEAM system invented by ISF RWTH Aachen. The Langmuir probe method is used for measurement. The relative simplicity of the method and the possibility of dispersion of high power on the probe allow its application for the investigation of high-power electron beams. The key element of the method is a rotating thin tungsten wire, which intersects the beam transversely on its axis and collects part of the current by itself. The signals, which are registered in the DIABEAM as a voltage, were taken in the form of amplitude. The conversion of the probe current into the distribution along the beam radius was realised using the Abel’s method. A voltage-current characteristic was built for the beam current. The local electron density as well as the electron temperature, the floating potential and the plasma potential were measured and calculated by means of this characteristic.
The laser beam-submerged arc hybrid welding method originates from the knowledge that, with increasing penetration depth, the laser beam process has a tendency to pore formation in the lower weld regions. The coupling with the energy-efficient submerged-arc process improves degassing and reduces the tendency to pore formation. The high deposition rate of the SA process in combination with the laser beam process offers, providing the appropriate choice of weld preparation, the possibility of welding plates with a thickness larger than 20° mm in a single pass, and also of welding thicker plates with the double-sided single pass technique.
In the face of the current trend towards larger and more complex production tasks in the SLM process and the current limitations in terms of maximum build space, the welding of SLM components to each other or to conventionally manufactured parts is becoming increasingly relevant. The fusion welding of SLM components made of 316L has so far been rarely investigated and if so, then for highly specialised laser welding processes. When welding with industrial gas welding processes such as MIG/MAG or TIG welding, distortions occur which are associated with the resulting residual stresses in the components. This paper investigates process-side influencing factors to avoid resulting residual stresses in SLM components made of 316L. The aim is to develop a strategy to build up SLM components as stress-free as possible in order to join them as profitably as possible with a downstream welding process. For this purpose, influencing parameters such as laser power, scan speed, but also scan vector length and different scan patterns are investigated with regard to their influence on residual stresses.