Poly(N-isopropylacrylamide) (PNIPAAm) hydrogel films with incorporated graphene oxide (GO) were developed and tested as light-stimulated actuators. GO dispersions were synthesized via Hummers method and characterized toward their optical properties and photothermal energy conversion. The hydrogels were prepared by means of photopolymerization. In addition, the influence of GO within the hydrogel network on the lower critical solution temperature (LCST) was investigated by differential scanning calorimetry (DSC). The optical absorbance and the response to illumination were determined as a function of GO concentration for thin hydrogel films. A proof of principle for the stimulation with light was performed.
Two types of microvalves based on temperature-responsive poly(N-isopropylacrylamide) (PNIPAAm) and pH-responsive poly(sodium acrylate) (PSA) hydrogel films have been developed and tested. The PNIPAAm and PSA hydrogel films were prepared by means of in situ photopolymerization directly inside the fluidic channel of a microfluidic chip fabricated by combining Si and SU-8 technologies. The swelling/shrinking properties and height changes of the PNIPAAm and PSA films inside the fluidic channel were studied at temperatures of deionized water from 14 to 36 °C and different pH values (pH 3–12) of Titrisol buffer, respectively. Additionally, in separate experiments, the lower critical solution temperature (LCST) of the PNIPAAm hydrogel was investigated by means of a differential scanning calorimetry (DSC) and a surface plasmon resonance (SPR) method. Mass-flow measurements have shown the feasibility of the prepared hydrogel films to work as an on-chip integrated temperature- or pH-responsive microvalve capable to switch the flow channel on/off.
Nacre-mimetic nanocomposites based on high fractions of synthetic high-aspect-ratio nanoclays in combination with polymers are continuously pushing boundaries for advanced material properties, such as high barrier against oxygen, extraordinary mechanical behavior, fire shielding, and glass-like transparency. Additionally, they provide interesting model systems to study polymers under nanoconfinement due to the well-defined layered nanocomposite arrangement. Although the general behavior in terms of forming such layered nanocomposite materials using evaporative self-assembly and controlling the nanoclay gallery spacing by the nanoclay/polymer ratio is understood, some combinations of polymer matrices and nanoclay reinforcement do not comply with the established models. Here, we demonstrate a thorough characterization and analysis of such an unusual polymer/nanoclay pair that falls outside of the general behavior. Poly(ethylene oxide) (PEO) and sodium fluorohectorite form nacre-mimetic, lamellar nanocomposites that are completely transparent and show high mechanical stiffness and high gas barrier, but there is only limited expansion of the nanoclay gallery spacing when adding increasing amounts of polymer. This behavior is maintained for molecular weights of PEO varied over four orders of magnitude and can be traced back to depletion forces. By careful investigation via X-ray diffraction and proton low-resolution solid-state NMR, we are able to quantify the amount of mobile and immobilized polymer species in between the nanoclay galleries and around proposed tactoid stacks embedded in a PEO matrix. We further elucidate the unusual confined polymer dynamics, indicating a relevant role of specific surface interactions.
Poly(vinyl acetate), PVAc, with a degree of polymerization Xn = 10 was prepared by chain-transfer radical polymerization using carbon tetrachloride and used as oligomeric plasticizer for commercial PVAc. However, the chlorinated chain ends cause a low thermal stability requiring mild Cl/H substitution. The product exhibits high thermal stability and excellent melt-compounding properties. Blends of oligomeric and commercial PVAc show single glass transition temperatures which decrease with higher oligomer content and exhibit small negative deviations from Fox' linear additivity rule. This indicates plasticization and miscibility being mainly due to entropic effects. Injection-moulded thick specimens show ductile behaviour at oligomer contents >10 wt %, while sheets with a thickness of 0.2–0.5 mm appear flexible already at 7.5 wt %. The oxygen permeability coefficients are an order of magnitude lower than those of low-density polyethylene. Due to the sum of their properties, the plasticized sheets present a promising alternative in the preparation of barrier materials.