Refine
Year of publication
- 2010 (342) (remove)
Institute
- Fachbereich Medizintechnik und Technomathematik (72)
- Fachbereich Wirtschaftswissenschaften (41)
- IfB - Institut für Bioengineering (40)
- Fachbereich Elektrotechnik und Informationstechnik (37)
- Fachbereich Energietechnik (35)
- Fachbereich Chemie und Biotechnologie (34)
- Fachbereich Maschinenbau und Mechatronik (31)
- Fachbereich Bauingenieurwesen (24)
- Fachbereich Luft- und Raumfahrttechnik (24)
- INB - Institut für Nano- und Biotechnologien (24)
Language
- English (185)
- German (155)
- Italian (1)
- Multiple languages (1)
Document Type
- Article (178)
- Conference Proceeding (73)
- Book (38)
- Part of a Book (20)
- Conference: Meeting Abstract (12)
- Patent (7)
- Report (5)
- Other (2)
- Part of a Periodical (2)
- Contribution to a Periodical (1)
Keywords
This paper aims to evaluate the formability of tailor welded blanks of dual phase (DP600)/transformation induced plasticity (TRIP700) steel sheets. In this work, bead on plate butt joints of 2·5 mm DP600 and 1·2 mm TRIP700 steel sheets were performed using CO2 laser beam welding. Microhardness measurements and transverse tensile testing were carried out to characterise the welds. The formability of base metals and welds were investigated by standard Erichsen test. In a perpendicular tensile test to the weld line, all specimens were fractured at the TRIP base metal, and the strengths were somewhat higher than those of base metal. There was a significant reduction in formability caused by welding of the DP600/TRIP700 steel sheets, and the formability increased with increasing welding speed.
Shielding gas influences on laser weldability of tailored blanks of advanced automotive steels
(2010)
The effects of shielding gas types and flow rates on CO2 laser weldability of DP600/TRIP700 steel sheets were studied in this work. The evaluated shielding gases were helium (He), argon (Ar) and different mixtures of He and Ar. Weld penetration, tensile strength and formability (Erichsen test) of laser welds were found to be strongly dependent upon the shielding gas types. The ability of shielding gas in removing plasma plume and thus increasing weld penetration is believed to be closely related to ionization potential and atomic weight which determine the period of plasma formation and disappearance. It was found that the higher helium shielding gas flow rate, the deeper weld penetration and the lower weld width.